Bambu PAHT-CF is a composite of PA12 and carbon fiber. Inheriting the advantages of low water absorption from PA12 and high-performance carbon fiber, Bambu PAHT-CF offers excellent mechanical and thermal properties that can be maintained well even when the prints get wet. Higher Z adhesion layers and flexibility make it ideal for creating engineering parts such as functional prototypes, machining fixtures, injection molds, jigs, and low-volume production parts.
Low water absorption
With a 50% lower water absorption rate compared to normal PA-CF,
Bambu PAHT-CF maintains excellent mechanical properties and dimensional stability even when exposed to high humidity.
Exceptional Z-bonding
Bambu PAHT-CF shows much higher adhesion in Z layers compared to normal PA-CF,
bringing it the ability to withstand high levels of impact or stress without breaking or deforming.
High tensile strength
Bambu PAHT-CF is designed to meet the demands of various industrial
and engineering applications where high strength and durability are required.
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System). Load and print! No more tedious setting steps.
Recommended Printing Settings
| Drying Settings (Blast Drying Oven) | 80 °C, 8 - 12 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 260 - 290 °C |
| Bed Temperature (with Glue) | 80 - 100 °C |
| Printing Speed | < 100 mm/s |
Physical Properties
| Density | 1.06 g/cm³ |
| Vicat Softening Temperature | 220 °C |
| Heat Deflection Temperature | 194 °C |
| Melting Temperature | 225 °C |
| Melt Index | 14.4 ± 2.0 g/10 min |
Mechanical Properties
| Tensile Strength | 92 ± 7 MPa |
| Breaking Elongation Rate | 8.4 ± 1.8 % |
| Bending Modulus | 4230 ± 210 MPa |
| Bending Strength | 125 ± 7 MPa |
| Impact Strength | 57.5 ± 3.4 kJ/m² |